Porting and valve seats
So I've been reading (and watching) a good deal about porting iron heads. And now have a decent understanding of the fluid dynamics, the porting theory etc... and of course I want to try my hand at it....
And as you'd expect from a 50 year old set of heads they look nothing like any tutorial--I can hardly make out the seat (maybe) from the rust. So I know this is the one area where flow really matters, and the one area where I can really eat it. So, I'm a bit stuck..I was going thinking I'd have the valves shaved and re-seated after porting in case I did nick a seat, but with the photo attached I really don't know where to start with these. Would you take them to the machine shop, have it all shot, square-decked, shaved, and then take it home do the porting and then go back to have them install new seats? |
#2
|
|||
|
|||
Decent drill motor, wire brush. Remove all loose carbon and rust. Will make the valve seats easier to see.
No sense putting ten cents of machine work into those heads until after you've played with the porting. You break-through into water, or the pushrod pinch, and you can just upend 'em into the recycle bin. |
The Following 2 Users Say Thank You to Schurkey For This Useful Post: | ||
#3
|
||||
|
||||
If you don’t know history of heads. Wire brush, take to machine shop have cleaned, check for excessive core shift, then magniflux before go any further
__________________
1963 Cat SD Clone (old school) streeter 1964 GTO post coupe, tripower, 4speed (build) 1965 GTO 389 tripower, 4 speed, driver 1966 GTO dragcar 1966 GTO Ragtop 1969 Tempest ET clone street/strip 1969 GTO Judge RA lll, auto 1969 GTO limelight Conv. 4speed go and show (sold) 1970 GP SSJ 1970 GTO barn find..TLB 390 horse? .yeh, 390 1972 GTO 455 HO, 4 speed, (build) 1973 Grand Safari wagon, 700hp stoplight sleeper 525ci DCI & 609ci LM V head builds |
The Following User Says Thank You to J.C.you For This Useful Post: | ||
#4
|
||||
|
||||
Do first what's posted in the above,that being getting them cleaned up, then glass beaded and then mag'ed.
You do not what to waste hours grinding only to later find out one or both may be cracked. I don't know what on line videos you have been watching, but 99% of all the ones I have seen are a waste of of time, all to many of these literal shade tree grinding good old boys do not even have a flow bench to prove out before and after flow numbers. Such a bunch of clowns only trying make some YouTube bucks off the video! Here's and simple 100% carved in stone rule to keep in mind about porting any head, it's easy math. It states Dx1.8 and relates to valve lift numbers vs flow. D is the diameter of the valve your working with. Example. Pontiac 2.11 Intake The math then produces a number of 379. This tells us that up to . 379" Intake valve lift the profile / angles of the the valve seat ( especially with a multi angle valve job) will control the level of flow produced, not for example the much talked about push rod pinch area or the sharp edge left on the short turn from the factory machining or casting. So if your running a Cam of let's say .500" lift then 67% of the air flow your getting is taking place up to that .379" lift, you don't want to unknowingly screw that up / demimish that unless you pick up enough higher lift flow to make up for the loss, especially in terms of Intake cfm numbers from .200" on up. Next the max hp you can make is determined by the minimum port area , do you know where that is in a Pontiac head?
__________________
Wernher Von Braun warned before his retirement from NASA back in 1972, that the next world war would be against the ETs! And he was not talking about 1/8 or 1/4 mile ETs! 1) 1940s 100% silver 4 cup tea server set. Two dry rotted 14 x 10 Micky Thompson slicks. 1) un-mailed in gift coupon from a 1972 box of corn flakes. Two pairs of brown leather flip flops, never seen more then 2 mph. Education is what your left with once you forget things! |
The Following User Says Thank You to steve25 For This Useful Post: | ||
#5
|
|||
|
|||
Thanks. So I'm mostly relying on Ch, 7 of the Jim Hand book -- am making a few sizing coins. I was not sure if a wire wheel would damage the seats...
When I mentioned videos, I really meant more of the theory for instance: https://www.youtube.com/watch?v=NlRX...THonde&index=1 Of course come across good ole boys, but trying to get beyond the basics and still marry with the practical application. |
#6
|
||||
|
||||
What casting number head is in your photo?
It’s hard to tell, but it looks like 6X-8, or maybe even a 6H casting off of a 455.
__________________
Wernher Von Braun warned before his retirement from NASA back in 1972, that the next world war would be against the ETs! And he was not talking about 1/8 or 1/4 mile ETs! 1) 1940s 100% silver 4 cup tea server set. Two dry rotted 14 x 10 Micky Thompson slicks. 1) un-mailed in gift coupon from a 1972 box of corn flakes. Two pairs of brown leather flip flops, never seen more then 2 mph. Education is what your left with once you forget things! |
#7
|
|||
|
|||
Quote:
They're 6x-4's. I was planning on following Jim Hand's book and then getting them shaved to about 84-85 cc. Although the book mentioned shaving upto 0.60" the machine shop I spoke to was already hesitant at taking 0.030" off. |
#8
|
|||
|
|||
I had .060 shaved off my 197 HOs and ran them for thirty years. Heads are still fine, never blew a head gasket.
|
#9
|
||||
|
||||
I have had and used the 4 series, 5 and 6 series ( 6X) milled .060 and have had no issues.
But whenever you mill them all the holes on the deck surface should get treated to a slight chamfer with a chamfering bit as in my photo. This especially needs to be done when milling has taken off more then .030 so as to deny a crack a place to start. I would also suggest you check on machine shop prices for milling a head more then .040 because at that point the cost for the needed milling of the intake flange the same amount will need to be factored in .
__________________
Wernher Von Braun warned before his retirement from NASA back in 1972, that the next world war would be against the ETs! And he was not talking about 1/8 or 1/4 mile ETs! 1) 1940s 100% silver 4 cup tea server set. Two dry rotted 14 x 10 Micky Thompson slicks. 1) un-mailed in gift coupon from a 1972 box of corn flakes. Two pairs of brown leather flip flops, never seen more then 2 mph. Education is what your left with once you forget things! |
The Following User Says Thank You to steve25 For This Useful Post: | ||
#10
|
|||
|
|||
Quote:
|
#11
|
||||
|
||||
With a 455 if you’re not intending to have a need to make peak hp above 5400 rpm then you do not need to step up to a 1.77” exh valve.
Just get a set of new intake and exh valves in the stock length for your 6X heads. If you mill your heads .045” or more you will need to check your valve train geometry to see if you need a different length push rods. Note, with stock 6X heads, 9.5 compression, a comp cams P-286-AH8 cam, a Q-jet and headers you would have to work at not making at least 370 Hp and 480 ft lbs . You need to run new valve springs and for this cam above you need the correct springs to handle the lift it produces. Also if your heads have more then 30K miles on them you can’t rerun your heads and expect good results. You need to at least having a shop freshen up the valve job. After doing the porting work guided by Jim’s book I would assume you would much closer to producing 400 Hp.
__________________
Wernher Von Braun warned before his retirement from NASA back in 1972, that the next world war would be against the ETs! And he was not talking about 1/8 or 1/4 mile ETs! 1) 1940s 100% silver 4 cup tea server set. Two dry rotted 14 x 10 Micky Thompson slicks. 1) un-mailed in gift coupon from a 1972 box of corn flakes. Two pairs of brown leather flip flops, never seen more then 2 mph. Education is what your left with once you forget things! Last edited by steve25; 06-07-2024 at 03:07 PM. |
The Following 2 Users Say Thank You to steve25 For This Useful Post: | ||
#12
|
|||
|
|||
Quote:
Quote:
It's a 400 (1976 557xxx block). Hone+stud the caps. Keep stock crank+rods Bore +0.040 with a 6.7 cc flat top piston. Melling SPC-7 (068) cam w/stock lift 6x-4 ported, valves re-cut etc (which was why I'm thinking I'd have them cut for 1.77" ex). Have heads shaved ~0.030" which hopefully will yield 85-87 cc chambers depending on what I read about casting tolerances, the valve job, and "deburing" the chamber. Planned to use the stock 1.5:1 rockers, was planning to use factory replacement valve springs...but I'm continuing to learn Use a 0.027" thin head gasket to get just north of 9:1 static CR. Either Q-jet or a Holley 750 on top. For now this will sit in front of a TH400 and a highway geared rear. This seemed like a fairly straight forward recipe similar to many in the back of Jim's book. |